Semiconductor device and manufacture method thereof

ABSTRACT

A semiconductor device includes a semiconductor substrate and at least one gate stack. The gate stack is present on the semiconductor substrate, and the gate stack includes at least one work function conductor and a filling conductor. The work function conductor has a recess therein. The filling conductor includes a plug portion and a cap portion. The plug portion is present in the recess of the work function conductor. The cap portion caps the work function conductor.

PRIORITY CLAIM AND CROSS-REFERENCE

This application is a continuation of and claims priority to U.S. Non-Provisional application Ser. No. 15/135,476, now titled “SEMICONDUCTOR DEVICE HAVING A FILLING CONDUCTOR COMPRISING A PLUG PORTION AND A CAP PORTION AND MANUFACTURING METHOD THEREOF” and filed on Apr. 21, 2016, which claims priority to U.S. Provisional Application Ser. No. 62/297,750, titled “FINFET METAL GATE ETCH BACK PROCESS” and filed on Feb. 19, 2016. U.S. Non-Provisional application Ser. No. 15/135,476 and U.S. Provisional Application Ser. No. 62/297,750 are incorporated herein by reference.

BACKGROUND

As the semiconductor industry has strived for higher device density, higher performance, and lower costs, problems involving both fabrication and design have been encountered. One solution to these problems has been the development of a fin-like field effect transistor (FinFET). A typical FinFET includes a thin vertical ‘fin’ formed by etching spaced recesses into a substrate. The source, drain, and channel regions are defined within this fin. The transistor's gate wraps around the channel region of the fin. This configuration allows the gate to induce current flow in the channel from three sides. Thus, FinFET devices have the benefit of higher current flow and reduced short-channel effects.

The dimensions of FinFETs and other metal oxide semiconductor field effect transistors (MOSFETs) have been progressively reduced as technological advances have been made in integrated circuit materials, and high-k metal gate (HKMG) processes have been applied to FinFETs.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 to FIG. 16 are cross-sectional views of a method for manufacturing a semiconductor device at various stages in accordance with some embodiments of the present disclosure.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

Examples of devices that can be improved from one or more embodiments of the present application are semiconductor devices. Such a device, for example, is a Fin field effect transistor (FinFET) device. The following disclosure will continue with a FinFET example to illustrate various embodiments of the present application. It is understood, however, that the application should not be limited to a particular type of device.

FIG. 1 to FIG. 16 are cross-sectional views of a method for manufacturing a semiconductor device at various stages in accordance with some embodiments of the present disclosure. Reference is made to FIG. 1. A substrate 110 is provided. In some embodiments, the substrate 110 includes silicon. Alternatively, the substrate 110 may include germanium, silicon germanium, gallium arsenide or other appropriate semiconductor materials. Also alternatively, the substrate 110 may include an epitaxial layer. For example, the substrate 110 may have an epitaxial layer overlying a bulk semiconductor. Further, the substrate 110 may be strained for performance enhancement. For example, the epitaxial layer may include a semiconductor material different from that of the bulk semiconductor, such as a layer of silicon germanium overlying bulk silicon or a layer of silicon overlying bulk silicon germanium. Such strained substrate may be formed by selective epitaxial growth (SEG). Furthermore, the substrate 110 may include a semiconductor-on-insulator (SOI) structure. Also alternatively, the substrate 110 may include a buried dielectric layer, such as a buried oxide (BOX) layer, such as that formed by separation by implantation of oxygen (SIMOX) technology, wafer bonding, SEG, or other appropriate method.

Semiconductor fins 112 and 114 are formed on the substrate 110. In some embodiments, the semiconductor fins 112 and 114 include silicon. The semiconductor fins 112 and 114 may be formed, for example, by patterning and etching the substrate 110 using photolithography techniques. In some embodiments, a layer of photoresist material (not shown) is sequentially deposited over the substrate 110. The layer of photoresist material is irradiated (exposed) in accordance with a desired pattern (the semiconductor fins 112 and 114 in this case) and developed to remove portions of the photoresist material. The remaining photoresist material protects the underlying material from subsequent processing steps, such as etching. It is noted that other masks, such as an oxide or silicon nitride mask, may also be used in the etching process.

An isolation dielectric 105 is formed to fill trenches between the semiconductor fins 112 and 114 as shallow trench isolation (STI). The isolation dielectric 105 may include any suitable dielectric material, such as silicon oxide. The method of forming the isolation dielectric 105 may include depositing an isolation dielectric 105 on the substrate 110 to cover the semiconductor fins 112 and 114, optionally performing a planarization process to remove the excess isolation dielectric 105 outside the trenches, and then performing an etching process on the isolation dielectric 105 until upper portions of the semiconductor fins 112 and 114 are exposed.

Gate dielectrics 122 and 124 are formed on the semiconductor fins 112 and 114 and the substrate 110, respectively. The gate dielectrics 122 and 124 may be formed by thermal oxidation, chemical vapor deposition, sputtering, or other methods known and used in the art for forming a gate dielectric. Depending on the technique of dielectric layer formation, the thickness of the gate dielectric 122 on the top of the semiconductor fin 112 may be different from the thickness of the gate dielectric 122 on the sidewall (not shown) of the semiconductor fin 112. Similarly, the thickness of the gate dielectric 124 on the top of the semiconductor fin 114 may be different from the thickness of the gate dielectric 124 on the sidewall (not shown) of the semiconductor fin 114. The gate dielectrics 122 and 124 can be patterned to respectively wrap central portions of the semiconductor fins 112 and 114 and respectively expose portions of the semiconductor fins 112 and 114. At least one of the gate dielectrics 122 and 124 may include, for example, a high-k dielectric material such as metal oxides, metal nitrides, metal silicates, transition metal-oxides, transition metal-nitrides, transition metal-silicates, oxynitrides of metals, metal aluminates, zirconium silicate, zirconium aluminate, or combinations thereof. In some embodiments, at least one of the gate dielectrics 122 and 124 may include hafnium oxide (HfO₂), hafnium silicon oxide (HfSiO), hafnium silicon oxynitride (HfSiON), hafnium tantalum oxide (HfTaO), hafnium titanium oxide (HfTiO), hafnium zirconium oxide (HfZrO), lanthanum oxide (LaO), zirconium oxide (ZrO), titanium oxide (TiO), tantalum oxide (Ta₂O₅), yttrium oxide (Y₂O₃), strontium titanium oxide (SrTiO₃, STO), barium titanium oxide (BaTiO₃, BTO), barium zirconium oxide (BaZrO), hafnium lanthanum oxide (HfLaO), lanthanum silicon oxide (LaSiO), aluminum silicon oxide (AlSiO), aluminum oxide (Al₂O₃), silicon nitride (Si₃N₄), oxynitrides (SiON), and combinations thereof. At least one of the gate dielectrics 122 and 124 may have a multilayer structure such as one layer of silicon oxide (e.g., interfacial layer) and another layer of high-k material. At least one of the gate dielectrics 122 and 124 may be formed using chemical vapor deposition (CVD), physical vapor deposition (PVD), atomic layer deposition (ALD), thermal oxide, ozone oxidation, other suitable processes, or combinations thereof.

Dummy gate layers 132 and 134 are respectively formed on the gate dielectrics 122 and 124. At least one of the dummy gate layers 132 and 134 may be formed by CVD, sputter deposition, or by other suitable technique for depositing conductive materials. The dummy gate layers 132 and 134 can be patterned to respectively wrap central portions of the semiconductor fins 112 and 114 and respectively expose portions of the semiconductor fins 112 and 114. In some embodiments, the gate dielectric 122 and the dummy gate layer 132 formed thereon may be patterned by the same process. Similarly, the gate dielectric 124 and the dummy gate layer 134 may be patterned by the same process. At least one of the dummy gate layers 132 and 134 may include polycrystalline-silicon (poly-Si) or poly-crystalline silicon-germanium (poly-SiGe).

Reference is made to FIG. 2. A pair of gate spacers 142 is formed on the substrate 110 and along the dummy gate structure 132, and a pair of gate spacers 144 is formed on the substrate 110 and along the dummy gate structure 134. In some embodiments, the gate spacers 142 and 144 may include silicon oxide, silicon nitride, silicon oxy-nitride, or other suitable material. The gate spacers 142 and 144 may include a single layer or multilayer structure. To form the gate spacers 142 and 144, a blanket layer may be formed on the substrate 110 by CVD, PVD, ALD, or other suitable technique. Then, an anisotropic etching is performed on the blanket layer to form the gate spacers 142 and 144 respectively on opposite sides of the dummy gate structures 132 and 134. In some embodiments, the gate spacers 142 and 144 are used to offset subsequently formed doped regions, such as source/drain regions. The gate spacers 142 and 144 may further be used for designing or modifying the source/drain region (junction) profile.

Reference is made to FIG. 3. Portions of the semiconductor fins 112 and 114 exposed both by the dummy gate structures 132 and 134 and the gate spacers 142 and 144 are removed (or recessed) to form recesses 112 r and 114 r in the substrate 110. Any suitable amount of material may be removed. The remaining semiconductor fin 112 has a plurality of source/drain portions 112 s and a channel portion 112 c between the source/drain portions 112 s. The remaining semiconductor fin 114 has a plurality of source/drain portions 114 s and a channel portion 114 c between the source/drain portions 114 s. The source/drain portions 112 s and 114 s are embedded in the substrate 110 and portions thereof are exposed by the recesses 112 r and 114 r. The channel portions 112 c and 114 c respectively underlie the dummy gate structures 132 and 134.

Removing portions of the semiconductor fins 112 and 114 may include forming a photoresist layer or a capping layer (such as an oxide capping layer) over the structure of FIG. 2, patterning the photoresist or capping layer to have openings that expose portions of the semiconductor fins 112 and 114, and etching the exposed portions of the semiconductor fins 112 and 114. In some embodiments, the semiconductor fins 112 and 114 can be etched using a dry etching process. Alternatively, the etching process is a wet etching process, or combination dry and wet etching process. Removal may include a lithography process to facilitate the etching process. The lithography process may include photoresist coating (e.g., spin-on coating), soft baking, mask aligning, exposure, post-exposure baking, developing the photoresist, rinsing, drying (e.g., hard baking), other suitable processes, or combinations thereof. Alternatively, the lithography process is implemented or replaced by other methods, such as maskless photolithography, electron-beam writing, and ion-beam writing. In yet some other embodiments, the lithography process could implement nanoimprint technology. In some embodiments, a pre-cleaning process may be performed to clean the recesses 112 r and 114 r with HF or other suitable solution.

Reference is made to FIG. 4. A plurality of epitaxy structures 152 and 154 are respectively formed in the recesses 112 r and 114 r and on the source/drain portions 112 s and 114 s of the semiconductor fins 112 and 114. The epitaxy structures 152 and 154 may be formed using one or more epitaxy or epitaxial (epi) processes, such that Si features, SiGe features, and/or other suitable features can be formed in a crystalline state on the source/drain portions 112 s and 114 s of the semiconductor fins 112 and 114. In some embodiments, the lattice constant of the epitaxy structures 152 and 154 are different from the lattice constant of the semiconductor fins 112 and 114, so that the channels of the semiconductor fins 112 and 114 can be strained or stressed by the epitaxy structures 152 and 154 to improve carrier mobility of the semiconductor device and enhance the device performance. The epitaxy processes include CVD deposition techniques (e.g., vapor-phase epitaxy (VPE) and/or ultra-high vacuum CVD (UHV-CVD)), molecular beam epitaxy, and/or other suitable processes. The epitaxy process may use gaseous and/or liquid precursors, which interact with the composition of the source/drain portions 112 s and 114 s of the semiconductor fins 112 and 114 (e.g., silicon). Thus, a strained channel can be achieved to increase carrier mobility and enhance device performance. The epitaxy structures 152 and 154 may be in-situ doped. The doping species include P-type dopants, such as boron or BF₂; N-type dopants, such as phosphorus or arsenic; and/or other suitable dopants including combinations thereof. If the epitaxy structures 152 and 154 are not in-situ doped, a second implantation process (i.e., a junction implant process) is performed to dope the epitaxy structures 152 and 154. One or more annealing processes may be performed to activate the epitaxy structures 152 and 154. The annealing processes include rapid thermal annealing (RTA) and/or laser annealing processes.

Thereafter, an interlayer dielectric (ILD) layer 160 is formed at outer sides of the gate spacers 142 and 144 and on the substrate 110. The ILD layer 160 includes silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, low-dielectric constant dielectric material or a combination thereof. The ILD layer 160 includes a single layer or multiple layers. The ILD layer 160 is formed by a suitable technique, such as CVD. A chemical mechanical planarization (CMP) process may be applied to remove excessive ILD layer 160 and expose top surfaces of the dummy gate structures 132 and 134 to a subsequent dummy gate removal process.

Reference is made to FIG. 5. The dummy gate structures 132 and 134 (see FIG. 4) are removed to form an opening 162 with the gate spacers 142 as its sidewall and an opening 164 with the gate spacers 144 as its sidewall. In some embodiments, the gate dielectrics 122 and 124 are removed as well. Alternatively, in some embodiments, the dummy gate structures 132 and 134 are removed while the gate dielectrics 122 and 124 retain as shown in FIG. 5. The dummy gate structures 132 and 134 (and the gate dielectrics 122 and 124) may be removed by dry etch, wet etch, or a combination of dry and wet etch. For example, a wet etch process may include exposure to a hydroxide containing solution (e.g., ammonium hydroxide), deionized water, and/or other suitable etchant solutions.

Reference is made to FIG. 6. A P-type work function material 172 can be formed on the structure shown in FIG. 5. The P-type work function material 172 can provide a desired work function value for a P-type gate stack of a P-type semiconductor device. The P-type work function material 172 can be formed by suitable process, such as ALD, CVD, PVD, remote plasma CVD (RPCVD), plasma enhanced CVD (PECVD), metal organic CVD (MOCVD), sputtering, plating, other suitable processes, and/or combinations thereof. In some embodiments, the P-type work function material 172 can be made of TiN, Co, WN, or TaC.

A dielectric material 240, e.g. spin-on-glass (SOG), can be formed, covering a portion of the P-type work function material 172 and filling the opening 164. A photoresist 245 can be defined over the dielectric material 240. The dielectric material 240 and/or the photoresist 245 can be provided for patterning the P-type work function material 172 for the P-type semiconductor device. The dielectric material 240 and the photoresist 245 can be defined by, for example, a spin-on process, a photolithographic process, and an etch process.

Reference is made to FIG. 7. A portion of the P-type work function material 172 that is not covered by the dielectric material 240 and the photoresist 245 of FIG. 6 can be removed, defining a P-type work function conductor layer 172 p. After defining the P-type work function conductor layer 172 p, the dielectric material 240 and the photoresist 245 of FIG. 6 can be removed by a wet etch process, a dry etch process, and/or combinations thereof, exposing the P-type work function conductor layer 172 p.

Reference is made to FIG. 8. An N-type work function material 174 can be formed on the structure shown in FIG. 7. The N-type work function material 174 can provide a desired work function value for an N-type gate stack of an N-type semiconductor device. The N-type work function material 174 can be formed by suitable process, such as ALD, CVD, PVD, remote plasma CVD (RPCVD), plasma enhanced CVD (PECVD), metal organic CVD (MOCVD), sputtering, plating, other suitable processes, and/or combinations thereof. In some embodiments, the N-type work function material 174 can be made of Ti, Al, or TiAl.

Reference is made to FIG. 9. a CMP process is applied to remove excessive portions of the P-type work function conductor layer 172 p and the N-type work function material 174 outside the openings 162 and 164 to provide a substantially planar top surface for the P-type work function conductor layer 172 p, the N-type work function conductor layers 174 n and 174 p. The remaining N-type work function conductor layer 174 n is present in the opening 162. The remaining P-type work function conductor layer 172 p and the N-type work function conductor layer 174 p are present in the opening 164.

Reference is made to FIG. 10. A mask 180 is formed on the structure shown in FIG. 9. In particular, the work function conductor in the opening 162, which includes the N-type work function conductor layer 174 n, has a recess R1 therein. The work function conductor in the opening 164, which includes the N-type work function conductor layer 174 p and the N-type work function conductor layer 172 p, has a recess R2 therein. The mask 180 may serve as a filling layer that is at least formed in the lower portions of the recesses R1 and R2. Such a filling layer may protect the underlying work function conductors from the subsequent etching process performed to the upper portions of the work function conductors. In some embodiments, the mask 180 overfills the recesses R1 and R2. In some embodiments, the mask 180 may be a hard mask, which includes silicon nitride, silicon oxynitride, silicon carbide, and/or other suitable materials. The mask 180 may be formed using methods such as CVD or PVD.

Reference is made to FIG. 11. Portions of the mask 180 are removed to expose at least top surfaces of the work function conductors in the opening 162 and 164, so as to benefit the subsequent etching process performed to the work function conductors in the openings 162 and 164. Stated differently, the mask 180 serving as the filling layer in the recesses R1 and R2 is recessed to expose portions of the work function conductors in the openings 162 and 164. In particular, the top surface of the N-type work function conductor layer 174 n in the opening 162 is exposed after the removing the overlying portion of the mask 180. Similarly, the top surfaces of the N-type work function conductor layer 174 p and the P-type work function conductor layer 172 p are exposed after the removing the overlying portions of the mask 180. In some embodiments, upper portions of the mask 180 are removed to expose at least top surfaces of the work function conductors, and lower portions of the mask 180 are remained in the recesses R1 and R2 to protect the underlying work function conductors after the removal process. An exemplary method of removing upper portions of the mask 180 may be an etching back process.

Reference is made to FIG. 12. The work function conductors in the opening 162 and 164 are recessed to expose at least portions of sidewalls 1422 and 1442 of the gate spacers 142 and 144. In particular, each of the gate spacers 142 has a sidewall 1422, and the sidewalls 1422 of the gate spacers 142 are opposite and define the opening 162 therebetween. The N-type work function conductor layer 174 n in the opening 162 and between the sidewalls 1422 of the gate spacers 142 is recessed, so that upper portions of the sidewalls 1422 are exposed. Similarly, each of the gate spacers 144 has a sidewall 1442, and the sidewalls 1442 of the gate spacers 144 are opposite and define the opening 164 therebetween. The N-type work function conductor layer 174 p and the P-type work function conductor layer 172 p in the opening 164 and between the sidewalls 1442 of the gate spacers 144 are recessed, so that upper portions of the sidewalls 1442 are exposed. After the recessing process, the top surface of the N-type work function conductor layer 174 n in the opening 162 may be shaped such that the recess R1 has a tapering opening R12 and a bottom recess R14 that are communicated with each other. The bottom recess R14 is present between the tapering opening R12 and the semiconductor fin 112. The tapering opening R12 tapers toward the bottom recess R14. In other words, the tapering opening R12 has a width greater than that of the bottom recess R14, and the width of the tapering opening R12 is spatially various. Similarly, after the recessing process, the top surfaces of the N-type work function conductor layer 174 p and the P-type work function conductor layer 172 p in the opening 164 may be shaped such that the recess R2 has a tapering opening R22 and a bottom recess R24 that are communicated with each other. The bottom recess R24 is present between the tapering opening R22 and the semiconductor fin 114. The tapering opening R22 tapers toward the bottom recess R24. In other words, the tapering opening R22 has a width greater than that of the bottom recess R24, and the width of the tapering opening R22 is spatially various. An exemplary method of the recessing the work function conductors may include a wet etching process that selectively removes portions of the work function conductors (e.g., work function metal pull back process) that are not protected by the mask 180.

Reference is made to FIG. 13. The mask 180 (see FIG. 12) in the recesses R1 and R2 are removed to expose the recesses R1 and R2. In other words, a portion of the work function conductor underlying the mask 180 and in the opening 162 (namely, a bottom portion of the N-type work function conductor layer 174 n) is exposed after this removal process. Similarly, a portion of the work function conductor underlying the mask 180 and in the opening 164 (namely, a bottom portion of the N-type work function conductor layer 174 p) is exposed after this removal as well. An exemplary method of removing the mask 180 in the recesses R1 and R2 is wet etching which is able to selectively remove silicon nitride, and this wet etching utilizes hot (approximately 145° C. to 180° C.) phosphoric acid (H₃PO₄) solutions with water.

Reference is made to FIG. 14. A filling conductor 190 is formed in the recess R1 and a space between the exposed portions of the sidewalls 1422 of the gate spacers 142. In some embodiments, the forming the filling conductor 190 includes overfilling the recess R1 with the filling conductor 190 such that the filling conductor 190 reaches the exposed portions of the sidewalls 1422 of the gate spacers 142, and therefore, the filling conductor 190 has a plug portion 192 (or a tail portion) and a cap portion 194 (or a head portion) connected to each other. The plug portion 192 is present in the recess R1 of the work function conductor in the opening 162. The cap portion 194 caps the work function conductor in the opening 162. In particular, the plug portion 192 occupies the recess R1 of the N-type work function conductor layer 174 n. The cap portion 194 caps the plug portion 192 and the N-type work function conductor layer 174 n and may contact with the sidewalls 1422 of the gate spacers 142. Such an N-type work function conductor layer 174 n and a filling conductor 190 may cooperatively serve as an N-type gate stack G1 for an N-type semiconductor device. In the N-type gate stack G1, since the cap portion 194 caps the N-type work function conductor layer 174 n, the contact area of the N-type gate stack G1 may be increased, which may benefit a contact formed on the N-type gate stack G1, especially the cap portion 194.

Similarly, a filling conductor 200 is formed in the recess R2 and a space between the exposed portions of the sidewalls 1442 of the gate spacers 144. In some embodiments, the forming the filling conductor 200 includes overfilling the recess R2 with the filling conductor 200 such that the filling conductor 200 reaches the exposed portions of the sidewalls 1442 of the gate spacers 144, and therefore, the filling conductor 200 has a plug portion 202 (or a tail portion) and a cap portion 204 (or head portion) connected to each other. The plug portion 202 is present in the recess R2 of the work function conductor in the opening 164. The cap portion 204 caps the work function conductor in the opening 164. In particular, the plug portion 202 occupies the recess R2 of the N-type and P-type work function conductor layers 174 p and 172 p. The cap portion 204 caps the plug portion 202 and the N-type and P-type work function conductor layer 174 p and 172 p, and it may contact with the sidewalls 1442 of the gate spacers 144. Such an N-type and P-type work function conductor layer 174 p and 172 p and a filling conductor 200 may cooperatively serve as a P-type gate stack G2 for a P-type semiconductor device. In the P-type gate stack G2, since the cap portion 204 caps the N-type and P-type work function conductor layer 174 p and 172 p, the contact area of the P-type gate stack G2 may be increased, which may benefit a contact formed on the P-type gate stack G2, especially the cap portion 204.

In some embodiments, since the cap portion 194 of the filling conductor 190 of the N-type gate stack G1 overfills the recess R1 to reach the opposite sidewalls 1422, the cap portion 194 has a width equal to the distance between the opposite sidewalls 1422. Similarly, since the cap portion 204 of the P-type gate stack G2 overfills the recess R2 to reach the opposite sidewalls 1442, the cap portion 204 has a width equal to the distance between the opposite sidewalls 1442. In some embodiments, the distance between the opposite sidewalls 1422 and the distance between the opposite sidewalls 1442 may be the same, so that the cap portions 194 and 204 of the N-type gate stack G1 and the P-type gate stack G2 have substantially the same width, which may benefit the cap portions 194 and 204 to push against the underlying work function conductors even if the work function conductors of the N-type gate stack G1 and the P-type gate stack G2 are different. In other words, even if the work function conductor of the N-type gate stack G1 includes the N-type work function conductor layer 174 n and the work function conductor of the P-type gate stack G2 includes both the N-type and P-type work function conductor layers 174 p and 172 p, the cap portions 194 and 204 having substantially the same width can provide optimized forces to push against the underlying work function conductors, respectively.

In some embodiments, since the work function conductor of the N-type gate stack G1 includes the N-type work function conductor layer 174 n, and the work function conductor of the P-type gate stack G2 includes both the N-type and P-type work function conductor layers 174 p and 172 p, the work function conductors of the N-type and P-type gate stacks G1 and G2 have different shapes, and therefore, the recesses R1 and R2 have different widths. As such, the plug portions 192 and 202 of the filling conductors 190 and 200 of the N-type and P-type gate stacks G1 and G2 have different widths.

In some embodiments, since the cap portions 194 and 204 are respectively formed by overfilling the recesses R1 and R2, and the plug portions 192 and 202 are respectively present in the recesses R1 and R2, the widths of the cap portions 194 and 204 are greater than that of the plug portions 192 and 202, which may benefit increasing the contact areas of the N-type and P-type gate stacks G1 and G2. Stated differently, the widths of the cap portions 194 and 204 are not less than that of the work function conductors in the openings 162 and 164 respectively, so that the contact areas of the N-type and P-type gate stacks G1 and G2 may be increased. In particular, the width of the cap portion 194 is not less than that of the N-type work function layer 174 n of the N-type gate stack G1, and the width of the cap portion 204 is that less than that of the P-type work function layer 172 p of the P-type gate stack G2.

In some embodiments, since the cap portions 194 and 204 are respectively formed by overfilling the recesses R1 and R2 to reach the sidewalls 1422 and 1442, the work function conductor in the opening 162 is absent on at least one sidewall of the cap portion 194, and the work function conductor in the opening 164 is absent on at least one sidewall of the cap portion 204 as well. In other words, the gate spacer 142 is present on at least one sidewall of the N-type gate stack G1, and the work function conductor of the N-type gate stack G1 (including the N-type work function conductor layer 174 n) is absent between the cap portion 194 and the gate spacer 142. Similarly, the gate spacer 144 is present on at least one sidewall of the P-type gate stack G2, and the work function conductor of the P-type gate stack G2 (including the N-type and P-type work function conductor layers 174 p and 172 p) is absent between the cap portion 204 and the gate spacer 144.

In some embodiments, since the plug portions 192 and 202 respectively occupy the recesses R1 and R2, the plug portions 192 and 202 may have shapes the same as that of the recesses R1 and R2. In particular, the plug portion 192 may include a tapering plug 1922 and a bottom plug 1924 connected to each other. The tapering plug 1922 is present between the cap portion 194 and the bottom plug 1924. The tapering plug 1922 occupies the tapering opening R12, and the bottom plug 1924 occupies the bottom recess R14. Therefore, the tapering plug 1922 tapers from the cap portion 194 to the bottom plug 1924. In other words, the tapering plug 1922 has a width greater than that of the bottom plug 1924, and the width of the tapering plug 1922 is spatially various. Similarly, the plug portion 202 may include a tapering plug 2022 and a bottom plug 2024 connected to each other. The tapering plug 2022 is present between the cap portion 204 and the bottom plug 2024. The tapering plug 2022 occupies the tapering opening R22, and the bottom plug 2024 occupies the bottom recess R24. Therefore, the tapering plug 2022 tapers from the cap portion 204 to the bottom plug 2024. In other words, the tapering plug 2022 has a width greater than that of the bottom plug 2024, and the width of the tapering plug 2022 is spatially various.

In some embodiments, the tapering plug 1922 and the sidewall 1422 of the gate spacer 142 define an angle α1 that ranges from about 0 degrees to about 90 degrees. In some embodiments, the angle α1 defined by the tapering plug 1922 and the sidewall 1422 of the gate spacer 142 may range from about 25 degrees to about 88 degrees, or from about 43 degrees to about 82 degrees, or about 67 degrees to about 79 degrees. Similarly, the tapering plug 2022 and the sidewall 1442 of the gate spacer 144 define an angle α2 that ranges from about 0 degrees to about 90 degrees. In some embodiments, the angle α2 defined by the tapering plug 2022 and the sidewall 1442 of the gate spacer 144 may range from about 25 degrees to about 88 degrees, or from about 43 degrees to about 82 degrees, or about 67 degrees to about 79 degrees. In some embodiments, the tapering plug 1922 and a sidewall of the bottom recess R14 define an angle β1 that ranges from about 90 degrees to 180 degrees. In some embodiments, the angle β1 defined by the tapering plug 1922 and the sidewall of the bottom recess R14 may range from about 102 degrees to about 163 degrees, or from about 115 degrees to about 154 degrees, or from about 120 degrees to about 146 degrees. Similarly, the tapering plug 2022 and a sidewall of the bottom recess R24 define an angle β2 that ranges from about 90 degrees to 180 degrees. In some embodiments, the angle β2 defined by the tapering plug 2022 and the sidewall of the bottom recess R24 may range from about 102 degrees to about 163 degrees, or from about 115 degrees to about 154 degrees, or from about 120 degrees to about 146 degrees.

In some embodiments, an exemplary method of forming the filling conductors 190 and 200 may include a deposition process such as CVD, PVD, ALD or other suitable process. After the deposition process, a CMP process may be applied to remove the excess filling conductors 190 and 200 that overfill outside the openings 162 and 164. In some embodiments, the filling conductors 190 and 200 are made by the same process and are made of substantially the same material. For example, the filling conductors 190 and 200 may include tungsten (W), aluminum (Al), copper (Cu) or other suitable conductive material.

Reference is made to FIG. 15. A portion of the filling conductor 190 in the space between the exposed portions of the sidewalls 1422 of the gate spacers 142 is recessed, and a portion of the filling conductor 200 in the space between the exposed portions of the sidewalls 1442 of the gate spacers 144 is recessed as well. More particularly, upper portions of the cap portions 194 and 204 are removed, and lower portions of the cap portions 194 and 204 respectively remain in the N-type and P-type gate stacks G1 and G2. An exemplary method of recessing portions of the filling conductors 190 and 200 may include an etching process. For example, the recessing includes reacting an etchant with the filling conductors 190 and 200, in which the etchant has high selectivity between the filling conductors 190, 200 and the gate spacers 142, 144.

Reference is made to FIG. 16. Dielectric caps 210 and 220 are respectively formed on the recessed filling conductors 190 and 200. In other words, the dielectric caps 210 and 220 respectively cap the recessed filling conductors 190 and 200. The dielectric cap 210 and the work function conductor of the N-type gate stack G1, which includes the N-type work function conductor layer 174 n, are spatially separated by the filling conductor 190. In particular, the cap portion 194 of the filling conductor 190 spatially separates the N-type work function conductor layer 174 n from the dielectric cap 210. Similarly, the dielectric cap 220 and the work function conductor of the P-type gate stack G2, which includes the N-type and P-type work function conductor layers 174 p and 172 p, are spatially separated by the filling conductor 200. In particular, the cap portion 204 spatially separates the N-type and P-type work function conductor layers 174 p and 172 p from the dielectric cap 220. In some embodiments, the width of the cap portion 194 is not less than that of the dielectric cap 210, so as to benefit the cap portion 194 to spatially separate the overlying dielectric cap 210 from the underlying N-type work function conductor layer 174 n. Similarly, the width of the cap portion 204 is not less than that of the dielectric cap 220, so as to benefit the cap portion 204 to spatially separate the overlying dielectric cap 220 from the underlying N-type and P-type work function conductor layers 174 p and 172 p.

An exemplary method of forming the dielectric caps 210 and 220 may include a deposition process, such as ALD, CVD, PVD or other suitable process. After the deposition process, a CMP process may be applied to remove the excess dielectric caps 210 and 220 that overfill outside the openings 162 and 164. The dielectric caps 210 and 220 may include silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, low-dielectric constant dielectric material or other suitable material.

In some embodiments, since the filling conductor includes the cap portion that caps the work function conductor, the cap portion may increase the contact area of the gate stack. Moreover, in some embodiments, since the cap portions (or head portions) of the filling conductors of the N-type and P-type gate stacks have substantially the same width, the cap portions may provide optimized forces to push against the underlying work function conductors of the N-type and P-type gate stacks.

In some embodiments, a semiconductor device includes a semiconductor substrate and at least one gate stack. The gate stack is present on the semiconductor substrate, and the gate stack includes at least one work function conductor and a filling conductor. The work function conductor has a recess therein. The filling conductor includes a plug portion and a cap portion. The plug portion is present in the recess of the work function conductor. The cap portion caps the work function conductor.

In some embodiments, a semiconductor device includes a semiconductor substrate, at least one N-type gate stack and at least one P-type gate stack. The N-type gate stack is present on the semiconductor substrate. The N-type gate stack includes a filling conductor therein. The filling conductor has a head portion and a tail portion. The tail portion is present between the head portion and the semiconductor substrate. The P-type gate stack is present on the semiconductor substrate. The P-type gate stack includes a filling conductor therein. The filling conductor has a head portion and a tail portion. The tail portion is present between the head portion and the semiconductor substrate. The head portions of the filling conductors of the N-type gate stack and the P-type gate stack have substantially the same width.

In some embodiments, a method of manufacturing a semiconductor device includes forming at least two gate spacers on a semiconductor substrate, forming at least one work function conductor between the gate spacers, the work function conductor having a recess therein, recessing the work function conductor between the gate spacers to expose at least portions of sidewalls of the gate spacers, and forming a filling conductor in the recess and a space between the exposed portions of the sidewalls of the gate spacers.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A semiconductor device, comprising: a first gate stack comprising: a first work function conductor; and a first filling conductor comprising a plug portion and a cap portion, wherein: the plug portion of the first filling conductor is disposed between a first sidewall of the first work function conductor and a second sidewall of the first work function conductor, and the cap portion of the first filling conductor overlies an uppermost surface of the first work function conductor; and a first gate spacer disposed on a first side of the first gate stack and a second gate spacer disposed on a second side of the first gate stack opposite the first side, wherein: a sidewall of the cap portion and the first sidewall of the first work function conductor are in direct contact with a sidewall of the first gate spacer.
 2. The semiconductor device of claim 1, the first gate stack comprising a second work function conductor disposed between the plug portion of the first filling conductor and the first sidewall of the first work function conductor and between the plug portion of the first filling conductor and the second sidewall of the first work function conductor.
 3. The semiconductor device of claim 2, wherein the first work function conductor is a p-type work function conductor and the second work function conductor is an n-type work function conductor.
 4. The semiconductor device of claim 1, comprising a dielectric cap, wherein the dielectric cap is separated from the first work function conductor by the cap portion of the first filling conductor.
 5. The semiconductor device of claim 1, comprising: a second gate stack comprising: the first work function conductor; a second work function conductor; and a second filling conductor comprising a plug portion and a cap portion, wherein: the plug portion of the second filling conductor is disposed between a first sidewall of the second work function conductor and a second sidewall of the second work function conductor, the plug portion of the second filling conductor is separated from the first work function conductor by the second work function conductor, and the cap portion of the second filling conductor overlies an uppermost surface of the first work function conductor and an uppermost surface of the second work function conductor.
 6. The semiconductor device of claim 5, wherein the first gate stack is a p-type gate stack and the second gate stack is an n-type gate stack.
 7. The semiconductor device of claim 1, comprising a semiconductor fin disposed below the first gate stack.
 8. The semiconductor device of claim 1, comprising: a second gate stack comprising the first work function conductor, wherein: a portion of the first work function conductor of the first gate stack has a first tapered profile, and a portion of the first work function conductor of the second gate stack has a second tapered profile different than the first tapered profile.
 9. A semiconductor device, comprising: a first gate spacer and a second gate spacer; and a gate stack disposed between the first gate spacer and the second gate spacer, the gate stack comprising: a gate dielectric in direct contact with the first gate spacer and the second gate spacer; a first work function conductor over the gate dielectric and in direct contact with the first gate spacer and the second gate spacer; and a filling conductor comprising a plug portion and a cap portion, wherein: the plug portion is disposed between a first sidewall of the first work function conductor and a second sidewall of the first work function conductor, and the cap portion caps the first work function conductor.
 10. The semiconductor device of claim 9, wherein the first work function conductor is in direct contact with a top surface of the gate dielectric.
 11. The semiconductor device of claim 9, wherein the cap portion of the filling conductor is in direct contact with the first gate spacer and the second gate spacer.
 12. The semiconductor device of claim 9, comprising: a dielectric cap, wherein the dielectric cap is separated from the first work function conductor by the cap portion of the filling conductor.
 13. The semiconductor device of claim 9, comprising a second work function conductor disposed between the first work function conductor and the plug portion of the filling conductor.
 14. The semiconductor device of claim 13, wherein the first work function conductor is disposed between the second work function conductor and the gate dielectric.
 15. A method of manufacturing a semiconductor device, the method comprising: forming a first gate spacer and a second gate spacer; forming a first work function conductor between the first gate spacer and the second gate spacer, wherein the first work function conductor defines a recess; forming a mask in a portion of the recess to conceal a first portion of the first work function conductor, wherein a second portion of the first work function conductor is not concealed by the mask; recessing the first work function conductor between the first gate spacer and the second gate spacer to expose a first portion of a sidewall of the first gate spacer and a first portion of a sidewall of the second gate spacer; removing the mask after the recessing the first work function conductor; forming a filling conductor in the recess and in a space between the first portion of the sidewall of the first gate spacer and the first portion of the sidewall of the second gate spacer; and recessing the filling conductor to expose a second portion of the sidewall of the first gate spacer and a second portion of the sidewall of the second gate spacer.
 16. The method of claim 15, wherein the recessing the first work function conductor comprises tapering some of the second portion of the first work function conductor.
 17. The method of claim 15, comprising: forming a dielectric cap between the second portion of the sidewall of the first gate spacer and the second portion of the sidewall of the second gate spacer.
 18. The method of claim 15, comprising: forming a second work function conductor between the first gate spacer and the second gate spacer before the forming a first work function conductor.
 19. The method of claim 18, comprising recessing the second work function conductor, wherein the recessing the second work function conductor comprises tapering some of the second work function conductor.
 20. The method of claim 18, wherein the first work function conductor is an n-type work function conductor and the second work function conductor is a p-type work function conductor. 